High bonding rate lightweight titanium clad aluminum with high temperature resistance
Titanium clad aluminum material belongs to the combination of non-ferrous metal and non-ferrous metal materials. Because of its high price, titanium is only used in aerospace, medical industry and ship industry. It has high strength, non-toxic and non-magnetic properties. ZEGOTA adopts innovative technology, high-end equipment and high-quality raw materials to develop and produce high-quality titanium clad aluminum plate & strip with leading high temperature resistance, lightweight and high strength.
Advantages:
1. Lightweight: Titanium density of 4.5g/cm3 and aluminum density of 2.7g/cm3. Titanium clad aluminum is the most lightweight and corrosion resistant material.
2. High Strength: Aluminum has superior mass-strength ratio. In lightweight design, titanium clad aluminum make full use of the high strength properties of aluminum.
3. High te1660℃, boiling point 3287℃, as a clad material, can withstand ex mperature resistance: Titanium melting point treme high temperature in surface contact.
Application:
1. Aerospace Industry: At the beginning of aircraft and rocket, the problem of high temperature and body weight caused by surface friction has not been solved. After the birth of titanium clad aluminum, the problem has been solved thoroughly because of its high temperature resistance and lightweight characteristics.
2. Medical industry: Titanium has the characteristics of non-toxicity, light weight and corrosion resistance. Aluminum has the characteristics of light weight, high strength and easy processing. At present, titanium clad aluminum are used in medical devices such as artificial joints, cardiac pacemakers, cardiovascular stents and so on.
3. Naval industry: Titanium clad aluminum are widely used in marine engineering due to their corrosion resistance, high strength and non-toxicity. Submarine field, such as submarine pressure hull, water jet propeller, sea water pipeline and other related equipment.
Parameter:
| Clad material |
Titanium |
Titanium |
Aluminum |
Titanium |
| Aluminum |
Aluminum |
Titanium |
Aluminum |
| Titanium |
/ |
/ |
/ |
| Thickness(mm) |
0.01-4.0 |
0.01-4.0 |
0.01-4.0 |
0.01-4.0 |
| Width(mm) |
5.0-1500 |
5.0-1500 |
5.0-1500 |
5.0-1500 |
| Tensile strength(MPa) |
150-180 |
250-320 |
150-180 |
250-320 |
| Yield strength(MPa) |
120-160 |
230-300 |
120-160 |
230-300 |
| Elongation(%) |
≥20 |
≥10 |
≥20 |
≥10 |
Product Tags:
|
|